性能项目试验条件[状态]测试方法测试数据数据单位 |
基本性能熔融指数200℃×5kgf(49N)ASTM D-1238(ISO 1133)1.6g/10min |
熔融指数220℃×10kgf(98N)ASTM D-1238(ISO 1133)17g/10min |
物理性能比重23℃/23℃ASTM D-792(ISO 1183)1.05 |
机械性能洛式硬度23℃ASTM D-785(ISO 2039/2)R-110R Scale |
弯曲模数23℃ASTM D-790(ISO 178)27000(2650)kg/cm2(MPa) |
弯曲强度23℃ASTM D-790(ISO 178)850(84)kg/cm2(MPa) |
IZOD冲击强度23℃(1/4"厚)ASTM D-256(ISO R180)20(196)kg.cm/cm(J/m) |
抗张强度23℃ASTM D-638(ISO 527)510(50)kg/cm2(MPa) |
热性能热变形温度Unannealed 18.6kg/cm2(1/2"厚)ASTM D-648(ISO 75/A)89℃ |
热变形温度Annealed(80℃×8hr)ASTM D-648(ISO 75/A)101℃ |
燃烧性FILE NO.E162823UL 941/16"HB All Color |
卫氏软化点1kg loadASTM D-1525(ISO 306)104℃ |